Controlling Porosity in 3D Printing with Activated Carbon https://ift.tt/2KLXtIu Researchers are getting even more in-depth with the study of materials and 3D printing with metal in the recently published, ‘Activated Carbon in the Third Dimension—3D Printing of a Tuned Porous Carbon.’ Seeking to create hierarchically structured porous carbons, the team of scientists from Technische Universität Darmstadt experimented with SLA 3D printing to create a new form of mechanically stable structures. Usually obtained in the form of powder, carbons may be classic black, activated, or nanomaterial. Often though, conductivity levels in these types of powder are low—causing ohmic losses and more constricted functionality for applications where more high surface area carbons are useful, such as:
The scientists expect that disadvantages with carbon materials can be overcome with the use of structures like monoliths, foams, and ‘regular open cellular structures.’ For structures requiring flexibility, on the other hand, other techniques can be employed like electron or laser melting, SLA, FFF 3D printing, and more. Previously, direct ink writing has shown great potential with graphene, but to improve control regarding porosity issues, the researchers endeavored to tune structures ‘on several scales.’ Printing a macroscopic structure, the researchers performed several steps, beginning with SLA 3D printing to control the part, while adding liquid porogen to cause phase separation and form a template. Once that is extracted, the polymer is stabilized with oxygen curing and then the final step of being pyrolyzed.
As the polymer is converted to carbon, the initial shape should still be maintained. The research team states that first a suitable monomer must be found. In this study, the three different monomers originally used were not suitable for the ‘envisioned synthesis strategy,’ however, a co-polymer made up of both an acrylate-based monomer and an aromatic monomer, yielded ‘synergistic effects.’ It was critical in the study, and resulting process, that copolymerization occur during photopolymerization—from within the SLA 3D printer, representing the only route for the slow-reacting DVB to be integrated. The researchers also stated that within this research they were not seeking parallel homopolymerization as it would separate the polymers and cause negative repercussions during pyrolysis.
While researchers for this study may have delved into more complex ways to create structures from carbon, many other uses have been discovered too, from carbon nanotube inks to carbon fiber composites, and even shape memory composites. What do you think of this news? Let us know your thoughts! Join the discussion of this and other 3D printing topics at 3DPrintBoard.com. [Source / Images: ‘ Activated Carbon in the Third Dimension—3D Printing of a Tuned Porous Carbon’] Please enable JavaScript to view the comments powered by Disqus. Printing via 3DPrint.com | The Voice of 3D Printing / Additive Manufacturing https://3dprint.com August 22, 2019 at 01:19AM
0 Comments
Leave a Reply. |
Categories
All
Archives
April 2023
|