Loughborough: Tests In Continuous Carbon Fiber Composites in 3D Printing With FDM and SLA http://bit.ly/2DLwhFZ UK researchers continue to explore the benefits of creating new composites for 3D printing. Here, they discuss their findings regarding carbon composites used in SLA 3D printing and material extrusion, outlined in their recently published paper, ‘Fabrication of the continuous carbon fiber reinforced plastic composites by additive manufacturing.’ As authors Y. Lu, G.K. Poh, A. Gleadall, L.G. Zhao, and X. Han explain, composites are often created due to a need for stronger mechanical properties in 3D printed and additive manufactured parts. Carbon is a material relied on especially in applications like the automobile industry and aerospace because of incredible strength, but also the potential for making lightweight parts that may not have been possible previously. The authors point out that while carbon fiber is useful for strengthening mechanical properties, it often still displays limited strength in tensile testing. This is due to a lack of control over short fibers, resulting in more unpredictable orientation and alignment during 3D printing. Beyond that, inferior bonding of the composite fibers and the matrix may also cause a lack of integrity in structures. In testing, the researchers used continuous-fiber-reinforced composites (CFRCs) in material extrusion and SLA processes. Testing was performed through physical evaluation of the mechanical properties, along with examination by microscope. Samples were created specifically for tensile testing, with Accura60 resin used for SLA 3D printing (with carbon fiber filament obtained from Markforged) and nylon and carbon fiber filament, also supplied by Markforged, used for material extrusion on a MarkTwo 3D printer. Tensile tests were then completed on an Instron 3369 machine with a 50 kN load cell, and then analyzed further through a Primotech microscope, with the fiber-matrix interface examined via a Hitachi TM3030 Tabletop scanning electron microscope.
While the elastic modulus was increased substantially with carbon fiber, the authors pointed out that it also significantly reduced elongation at break, due to a lower elongation-to-break—in comparison to the use of all nylon material. Because of this, the sample was brittle. They also noticed high porosity due to voids in the fiber/matrix layers—leading to decreased mechanical performance. It was noted that this could be due to inferior infill density, with printed fibers not being even distributed during 3D printing—leading to ‘compromised’ tensile properties.
One of the most fascinating parts of 3D printing is not only the innovations that spring forth from the technology continually, but also the ongoing refinements in machines and materials. And while one type of plastic or metal may be suitable for a range of applications, users often find that by adding another material or element, they can strengthen or stabilize parts further, whether in using metals like titanium or a mixture of graphene and alginate, or recycling wood into 3D printed composites. What do you think of this news? Let us know your thoughts! Join the discussion of this and other 3D printing topics at 3DPrintBoard.com. [Source / Images: ‘ Fabrication of the continuous carbon fiber reinforced plastic composites by additive manufacturing’] Printing via 3DPrint.com | The Voice of 3D Printing / Additive Manufacturing https://3dprint.com April 26, 2019 at 10:54AM
0 Comments
Leave a Reply. |
Categories
All
Archives
April 2023
|